The invention relates to a preparation method of polyester resin for weather resistant powder coating, relating to the technical field of outdoor powder coating production, in particular to the processing technology field of polyester resin for producing paint. The invention is mainly composed of polyol and polybasic acid and condensation, removal of water through the reaction and generate the esterification reactions constantly, so as to obtain certain degree of polymerization of polyester resin polymer. Polyester resin will be produced for the production of outdoor powder coating, can make the surface of the product has the advantages of high gloss and excellent resistance to weathering, the weather aging resistance test, qualified can reach 1600h.
【技術實現步驟摘要】
耐候型粉末涂料用聚酯樹脂的制備方法
本專利技術涉及耐候性粉末涂料生產
，特別是生產涂料用的聚酯樹脂的加工工藝
技術介紹
現有的采用聚酯樹脂制成的粉末涂料用于室外使用的物件噴涂時，在自然條件下，一長般耐候性難以滿足高標準要求，在耐人工氣候老化性試驗中，只能達到800h合格，無粉化、起泡、開裂、剝落等異常現象。
技術實現思路
本專利技術目的在于提出一種可用于生產耐候性強的粉末涂料的聚酯樹脂的制備方法。本專利技術包括以下步驟：1、將反應釜溫度升至80℃，然后投入新戊二醇、對苯二甲酸、三羥甲基丙烷和單丁基氧化錫；2、將反應釜溫度按2-3℃/15分鐘升溫速率升至240℃，在240℃下反應100～120分鐘；3、投入間苯二甲酸后在240℃下反應120～180分鐘；4、在0.090～0.095mPa真空下進行縮聚反應180～240分鐘；5、將反應釜降溫至180～200℃加入三苯基膦，反應30±2分鐘出料，出料，取得聚酯樹脂；所述反應過程的各原料投料質量比為新戊二醇35～45份、三羥甲基丙烷1～3份、對苯二甲酸10～20份、間苯二甲酸50～70份、單丁基氧化錫0.2～0.5份、三苯基膦1～3份。本專利技術主要由多元醇與多元酸縮合而成，通過反應生成水的去除而使酯化反應不斷進行，從而獲得一定聚合度的高分子聚酯樹脂。將本專利技術方法生產的聚酯樹脂用于生產粉末涂料，可使產品表面具有高光澤和優越的戶外耐候性等優點，在耐人工氣候老化性試驗中，可達到1600h合格。具體實施方式：一、稱量（重量份）：分別稱取新戊二醇35～45份、三羥甲基丙烷1～3份、對苯二甲酸10～20份、...
【技術保護點】
耐候型粉末涂料用聚酯樹脂的制備方法，其特征在于包括以下步驟?：?將反應釜溫度升至?80℃，然后投入新戊二醇、對苯二甲酸、三羥甲基丙烷和單丁基氧?化錫?；?將反應釜溫度按?2?3℃?/15?分鐘升溫速率升至?240℃，在?240℃下反應?100?～?120?分?鐘?；?投入間苯二甲酸后在?240℃下反應?120?～?180?分鐘?；?在?0.090?～?0.095mPa?真空下進行縮聚反應?180?～?240?分鐘?；?將反應釜降溫至?180?～?200℃加入三苯基膦，反應?30±2?分鐘出料，出料，取得聚酯?樹脂?。
【技術特征摘要】
1.耐候型粉末涂料用聚酯樹脂的制備方法，其特征在于包括以下步驟：將反應釜溫度升至80℃，然后投入新戊二醇、對苯二甲酸、三羥甲基丙烷和單丁基氧化錫；將反應釜溫度按2-3℃/15分鐘升溫速率升至240℃，在240℃下反應100～120分鐘；投入間苯二甲酸后在240℃下反應120～180分鐘；在0.090～0.0...
【專利技術屬性】
技術研發人員：謝海，
申請(專利權)人：江蘇冠軍涂料科技集團有限公司，
類型：發明
國別省市：江蘇,32