一種封頭的清洗方法技術
Method for cleaning head
The invention relates to a cleaning method of a head cover, which is characterized in that the method comprises the following steps: (1) the head cap is sprayed with an organic matter detergent to lay 30min at a temperature of between 20 and 45 DEG C. (2) the head is immersed in the sodium borate solution of 3%, and (3) the head is immersed in a compound surfactant to be treated. The advantages of the invention are: simple operation, convenient maintenance, long range effect, good cleaning quality, high efficiency, good compatibility, the process parts after surface cleaning clean, does not affect the part precision and surface state, non-toxic, no smell, no harm to the health of operation.
【技術實現步驟摘要】
本專利技術主要涉及一封頭,尤其涉及一種封頭的清洗方法。
技術介紹
封頭，是石油化工、原子能到食品制藥諸多行業壓力容器設備中不可缺少的重要部件，主要用于各種容器設備，材質主要是以不銹鋼、碳鋼、合金鋼、鋁、鈦、銅、鎳及鎳合金等。在壓力容器中封頭的材料主要以鋁合金為主。不銹鋼封頭在制作成形、焊接、施工等過程中會帶來表面油污、鐵銹、非金屬臟物等，影響了封頭的使用壽命，因此要處理表面污垢，以免在實用過程中導致封頭不能正常使用。
技術實現思路
本專利技術的目的是克服上述現有工藝存在的不足，而提供一種封頭的清洗方法。本專利技術的技術方案是：清潔封頭的制作方法，其步驟為：將封頭噴淋有機物助洗劑在溫度為20—45℃下放置30min，之后在用清水沖洗。將封頭浸泡在3％的硼酸鈉溶液進行處理，處理溫度為20—55℃，處理時間為15-25min，之后用清水沖洗。將封頭浸泡復合表面活性劑進行處理，處理溫度為20-50℃，處理時間為30min，之后，再用清水沖洗。本專利技術的優點是：操作簡便、效程持久、使用維護方便、清洗質量好、效率高、工藝兼容性好、經清洗后的零件表面潔凈、不影響零件的尺寸精度和表面狀態、無毒、無刺激性氣味、不危害操作者身體健康。具體實施例下面結合一個實施例，對本專利技術提供一種封頭的清洗方法進行詳細的說明。清潔封頭的制作方法，其步驟為：將封頭噴淋有機物助洗劑在溫度為20—45℃下放置30min，之后在用清水沖洗。將封頭浸泡在3％的硼酸鈉溶液進行處理，處理溫度為20—55℃，處理時間為15-25min，之后用清水沖洗。將封頭浸泡復合表面活性劑進行處理，處理溫度為20-50...
【技術保護點】
一種封頭的清洗方法，其特征在于步驟為：包括以下步驟：(1)將封頭噴淋有機物助洗劑在溫度為20—45℃下放置30min，之后在用清水沖洗。(2)將封頭浸泡在3％的硼酸鈉溶液進行處理，處理溫度為20—55℃，處理時間為15?25min，之后用清水沖洗。(3)將封頭浸泡復合表面活性劑進行處理，處理溫度為20?50℃，處理時間為30min，之后，再用清水沖洗。
【技術特征摘要】
1.一種封頭的清洗方法，其特征在于步驟為：包括以下步驟：(1)將封頭噴淋有機物助洗劑在溫度為20—45℃下放置30min，之后在用清水沖洗。(2)將封頭浸泡在3％的硼酸鈉溶液進行...