The invention discloses a concrete water reducing agent, which comprises a vinyl acetate ethylene copolymer powder, fatty acid soap, melamine formaldehyde resin of sodium silicate solution, which has good sphericity powder dispersed in aqueous solution and evenly dispersed in alkaline conditions, fatty acid soap as interface modification agent can make the dispersible powder surface properties change, the rubber powder surface and the adsorbed water molecules to form a water film, this film of water has a very good lubrication, and melamine formaldehyde resin has good hydrophilicity, can reduce agglomeration in water cement water reducing effect.
【技術實現步驟摘要】
一種水泥減水劑
本專利技術屬于建材
，涉及一種水泥減水劑。技術背景近年來，混凝土在我國工程建設中發揮了重要作用。由于減水劑能有效地改善混凝土的性能，而且具有良好的經濟效益，在許多國家都得到廣泛應用，高效減水劑在工程中的應用越來越受到重視，成為混凝土中不可或缺的材料。減水劑經歷了從木素磺酸鹽、萘磺酸鹽縮合物（奈系減水劑）、脂肪族及聚羧酸系等發展的歷程，木素磺酸鹽為最常用的普通減水劑，但該減水劑再攪拌過程中易造成緩凝，常引入大量空氣而影響混凝土的性能；奈系減水劑在和成過程不可避免的硫酸鈉含量的居高不下，進而導致外加劑中堿含量增高，混凝土的耐久性降低，眾多工程出現堿骨料反應現象，使用壽命大幅縮短。此外，芳香族磺酸鹽對人體和生物具有潛在的毒性。脂肪族減水劑生產所用的原材料甲醛丙酮等單體配比難以控制造成減水劑性能變差，與水泥基體產生相容性問題。現有聚羧酸減水劑成本高，合成過程中聚合度存在差異，使其性能存在差異；此外，我國砂石供需矛盾突出，天然砂逐漸被機制砂取代，然而機制砂在粒形，級配，表面質構以及0.075mm的石粉顆粒相比天然砂都有較大的區別，導致減水劑失效或減水效率下降，進而對混凝土性能產生重大影響。
技術實現思路
本專利技術的目的在于，克服現有技術的不足，提供了一種成本低、效率高的減水劑，本專利技術的減水劑減水率高、流動性好，可明顯改善混凝土流動性和工作度，減水率可達20-30%。與混凝土有良好相容性，且對水泥混凝土的強度影響不大。為了解決上述技術問題，本專利技術所采取的技術方案如下：一種水泥減水劑，按照重量份數計它由以下組份組成：醋酸乙烯酯與乙烯共聚膠...
【技術保護點】
一種水泥減水劑，其特征在于按照重量份數計它由以下組份組成：醋酸乙烯酯與乙烯共聚膠粉20份，脂肪酸鉀皂15份、三聚氰胺甲醛樹脂15份、硅酸鈉溶液20份。
【技術特征摘要】
1.一種水泥減水劑，其特征在于按照重量份數計它由以下組份組成：醋酸乙烯酯與乙...