The present invention provides a method for removing calcium impurities in high purity magnesium nitrate, which comprises the following steps: (1) dissolved in nitric acid solution in the analysis of pure pure Magnesium Oxide analysis, after the completion of dissolution with hydrofluoric acid; (2) analysis of the use of pure Magnesium Oxide regulating PH = 7.5-8, 3-8min static 1-3H, stirring, filtering, concentrating a solution to the proportion of 1.4-1.42; (3) cooling to room temperature, separation and crystallization; the method after simple treatment can achieve effective removal efficiency, avoid duplication of concentration and crystallization of the treatment effect is good, the high pure grade reagent with magnesium nitrate standard, has a wide application prospect.
【技術實現步驟摘要】
一種高純度硝酸鎂中去除鈣雜質的方法
本專利技術涉及一種雜質處理工藝，尤其是一種高純度硝酸鎂中去除鈣雜質的方法。
技術介紹
高純硝酸鎂一般使用稀硝酸和分析純氧化鎂，經中和、結晶制備，分析純氧化鎂中，鈣(Ca)的含量一般為0.02％，而使用高純氧化鎂，成本較高，因此通常制備高純硝酸鎂時，反復重結晶耗時長、能耗高、損耗大，經濟性較差。因此，尋找一種方便有效的去除硝酸鎂中含鈣雜質的方法具有非常重要的生產實踐意義。
技術實現思路
本專利技術所要解決的技術問題在于提供一種高純度硝酸鎂中去除鈣雜質的方法。為解決上述技術問題，本專利技術的技術方案是：一種高純度硝酸鎂中去除鈣雜質的方法，具體步驟為：(1)分析純氧化鎂溶于分析純硝酸溶液中，溶解完成后加入氫氟酸；(2)使用分析純氧化鎂調節PH＝7.5-8，攪拌3-8min，靜置1-3h，過濾，將溶液濃縮至比重1.4-1.42；(3)冷卻至室溫，分離結晶。優選的，上述高純度硝酸鎂中去除鈣雜質的方法，具體步驟為：(1)分析純氧化鎂每400g，溶于2.5kg25％分析純硝酸溶液(630g，以HNO3計)中，溶解完成后，加入氫氟酸1g(按HF計)；(2)使用分析純氧化鎂調節PH＝7.5-8，攪拌5min，靜置2h，過濾，將溶液濃縮至比重1.4-1.42；(3)冷卻至室溫，分離結晶。上述高純度硝酸鎂中去除鈣雜質的方法原理如下：MgF2,Ksp＝6.4×10-9，18℃溶解度87mg/L，折0.0087g/100ml；CaF2，Ksp＝2.7×10-11，18℃溶解度16mg/L，折0.0016g/100ml；兩者在弱堿性條件下均難溶于水。因...
【技術保護點】
一種高純度硝酸鎂中去除鈣雜質的方法，其特征在于：具體步驟為：(1)分析純氧化鎂溶于分析純硝酸溶液中，溶解完成后加入氫氟酸；(2)使用分析純氧化鎂調節PH＝7.5?8，攪拌3?8min，靜置1?3h，過濾，將溶液濃縮至比重1.4?1.42；(3)冷卻至室溫，分離結晶。
【技術特征摘要】
1.一種高純度硝酸鎂中去除鈣雜質的方法，其特征在于：具體步驟為：(1)分析純氧化鎂溶于分析純硝酸溶液中，溶解完成后加入氫氟酸；(2)使用分析純氧化鎂調節PH＝7.5-8，攪拌3-8min，靜置1-3h，過濾，將溶液濃縮至比重1.4-1.42；(3)冷卻至室溫，分離結晶。2.根據權利要求1所述的高純度硝酸鎂中去...
【專利技術屬性】
技術研發人員：林利成，蘇學松，
申請(專利權)人：天津市科密歐化學試劑有限公司，
類型：發明
國別省市：天津,12
還沒有人留言評論。發表了對其他瀏覽者有用的留言會獲得科技券。